- 2610000000铬矿
- 物理破碎|灰褐色,粉状|铸造,生产铁合金|CR2O3:41.96%,FEO:26.92%,水份:4.08%,AL2O3:16.05%MGO:10.31%,CAO:0.16%,SIO2:3.06%,P:0.004%,S:0.002%,CR:FE:1.37:1|天然开采|Size:0-1MM,99.91%
- 2610000000铬矿
- 物理破碎|灰褐色,粉状|铸造:生产铁合金|CR2O3:42.17%,FEO:27.06%,水份:3.3%,AL2O3:16.35%MGO:9.15%,SIO2:3.14%,P:0.003%,S:0.002%,CR:FE:1.37:1|天然开采|Size:-1MM,99.57%
- 2601112000铁矿粉
- 炼钢用|破碎和粉磨|黑色粉状|铁:63.02%,水分:6.14%,硫:0.17%,磷:0.04%,二氧化硅:5.13%,三氧化二铝:0.7%|0.8MM-6.3MM|平均粒度及成分等待进一步检测|未烧结
- 2610000000铬矿(冶金级)
- 加工方法:铸造|外观:深褐色,粉状|用途:铸铬铁|成分含量:CR2O3:42.05%,MgO:9.33%,水份:5.11%,AL2O3:15.28%,SIO2:3.04%,P:0.002%,S:0.003%,FE2O3:20%,CR:FE=1.34:1|来源:天然开采|Size:0-1MM99.97%
- 2610000000铬矿砂
- 加工方法开采，粉碎|外观黑褐色粉状|用途冶炼用|成分含量Cr:26%,水分5%.FE:10%P<0.01%S<0.02%|来源天然矿山开采|CR:FE:1.4
- 2602000000锰矿
- 加工硅锰铁|天然矿经筛选、去尘、去杂质及水洗,未烧结|灰黑色,粉状|Mn:38.01%,MnO2:53.21%,Fe:14.73%P:0.054%,SIO2:11.29%,AL2O3:0.91%,水份:9.10%|天然开采|Size:0-10mm99.91%
- 2602000000天然锰
- 用于制造二氧化锰干电池;粉碎网筛和电磁分离;粉状;二氧化锰85%铁2.7%矾土4%氯化氢5%水3%镍钴铜0.3%;
- 2602000000天然锰
- 用于制造二氧化锰干电池;粉碎网筛和电磁分离;粉状;二氧化锰85%铁2.7%矾土4%氯化氢5%水3%镍钴铜0.3%;锰矿
- 2610000000铬矿
- 物理破碎|灰褐色,粉状|铸造:生产铁合金|CR2O3:41.2%,FEO:26.83%,水份:4.63%,AL2O3:15%,SIO2:4.31%,P:0.003%,S:0.005%,CR:FE:1.35:1|天然开采|Size:0-1.0MM90%
- 2804690000硅粉
- 用于电子产品原料|加工方法:碾压成粉状未掺杂|成分含量:Si99.091%,Fe0.4%,Al0.4%,Ca0.1%,P0.005%,B0.004%|WALLPARK牌|签约日期:2012年3月30日,粒度75-850微米|牌号:441,非易制毒,非两用物项商品
专业提供各国海关进出口数据、各国贸易数据、产品进出口分析报告、 行业进出口报告、企业进出口报告、进口企业黄页、出口企业黄页等信息产品
-
有需求者请致电：010-89438819
微信公众号：CIE-DATA
-
关注公众号
网站简介 | 帮助中心 | 网站建设 | 订购广告 | 网站律师 | 付款方式 | 服务条款 | 隐私保护 | 联系我们
服务热线：010-89438819 京ICP备12042581-2
进出口服务网(www.ciedata.com)版权所有 2009
服务热线：010-89438819 京ICP备12042581-2
进出口服务网(www.ciedata.com)版权所有 2009