- 2610000000铬精粉
- 破碎|灰褐色粉状|铸造铬铁|CR2O3:42.32%CR:FE=1.38:1FEO:26.99%SIO2:2.50%H2O:6.29%AL2O3:15.77%MGO:9.77%P:0.005%S:0.004%SIZE:0-1MM99.98%散装入柜|天然矿
- 2610000000铬精矿
- 加工方法:原矿未加工|外观:灰黑色粉状|用途:铸造|含量:CR2O3:41.17%CR/FE:1.35:1|来源:矿山开采
- 2610000000铬矿
- 采掘、筛选|黑色粉状|铸造,生产铁合金|CR2O3:42.42%,CR:FE:1.39:1,水份:4.35%,SIO2:2.71%,AL2O3:15.72%,MGO:9.84%,粒度:-1MM99.89%|原矿开采
- 2610000000铬矿
- 加工方法：原矿|外观：黑灰色粉状|用途：冶金用|成分含量：CR2O3:20.9%CR/FE:3.4/1|来源：天然
- 2610000000铬矿
- 破碎|黑褐色粉状|加工铬铁用|CR2O3:43.09%|开采|Cr/Fe:Ratio:1.53:1,SIO2:3.84%,AL2O3:14.87%,MgO:10.32%,CaO:5.62%,Moisture:4.02%,P:0.003%,S:0.004%,SIZE:below1mm:99.34%
- 2601112000FMG低品位粉铁矿
- 炼钢用|加工方法:原矿开采未经烧结|粉状|Fe57.51%水8.7%|平均粒度0.8-6.3MM|制造商：FMG
- 2601112000毛里塔尼亚粉矿（未烧结铁矿砂）
- 炼钢用|未烧结，碾碎|褐黑色粉状|FE:62.87%,SIO2:8.08%,AL2O3:0.82%,S:0.009%,P:0.067%,含水率:2.10%|0.8MM<平均粒度<6.3MM
- 2601112000铁矿粉
- 用途:炼铁用|加工方法:未烧结|外观:红褐色粉状|成分含量:Fe:58.63%|平均粒度:5.2013MM
- 2601112000铁矿粉
- 用途:炼铁用|加工方法:未烧结|外观:红褐色粉状|成分含量:Fe:58.79%;|平均粒度:5.2122MM
- 2601112000铁矿粉
- 炼铁用|磨碎|粉状|Fe:61.74%|平均粒度不小于0.8但不大于6.3mm|未烧结,澳大利亚粉矿|干吨:93013.571
专业提供各国海关进出口数据、各国贸易数据、产品进出口分析报告、 行业进出口报告、企业进出口报告、进口企业黄页、出口企业黄页等信息产品
-
有需求者请致电：010-89438819
微信公众号：CIE-DATA
-
关注公众号
网站简介 | 帮助中心 | 网站建设 | 订购广告 | 网站律师 | 付款方式 | 服务条款 | 隐私保护 | 联系我们
服务热线：010-89438819 京ICP备12042581-2
进出口服务网(www.ciedata.com)版权所有 2009
服务热线：010-89438819 京ICP备12042581-2
进出口服务网(www.ciedata.com)版权所有 2009